I have DSC for Al-Ti alloy and its composites with MgO and SiC and there are shifting in peaks to upper or lower regions, Please can any one help me to interpret them?
I think the peak which shifted to upper became more exothermic and the peak shifted to lower region became loss exothermic.
Please, draw all signals on one plot. and provide some additional information - what is the gaseous enviroment, sample masses (if different in these three runs), confinemtn of the sample (open/pierced/closed pan)
In addition to Nikita's comments: please indicate if this is raw data or if you have already substracted the baseline. If no, please do so. This would explain the tendency of your curves going upwards/downwards (not including the exo/endo peaks).
Dear Rana Afif Majed Anaee,
In addition to the question of Alexander Pisch I have some other points:
* The temperature correction is properly performed?
* What is the composition and the heat treatment condition of your Al-Ti or Ti-Al alloy?
* What is the volume fraction of the reinforcing particles MgO and SiC?
* The DSC is performed on heating or cooling at what rates?