Dear Researchers,

I have tried electro-spinnning of PVDF powder using DMF and Acetone with small concentration of LiCl.

I used 20 -30 Kv and varied distances and flow-rates. However, I couldn't find any nanofiber.

Some paper suggested 14 wt% PVDF, 60 wt % DMF, 26wt % Acetone and 0.05 gm LiCl. However this resulted in low viscosity solution. Then I gradually added PDVF until I reached in a reasonable thickness. See attached image.

When I charged this solution in the electro-spinning at 30 Kv, the liquid front looked like the attached image.

Can any one suggest what might be issue behind this?

I appreciate your suggestions,

Thanks and Regards,

Rahman