6 Questions 2 Answers 0 Followers
Questions related from Sc Park
When a Fe-3.5wt% Si cast sample was heat-treated at 1,350°C for 2 hours, the permeability doubled. SEM and XRD comparisons showed no difference, so the cause is unknown. Please explain why the...
19 August 2025 3,008 4 View
The residual stress of the additive manufactured aluminum alloy was measured using neutron diffraction (refer to the picture below for the sample shape). The residual stress result measured by...
13 February 2023 348 1 View
The AlSi7Mg sample was additive manufacturing by the PBF method and heat treated 480℃-6h and 550℃-6h. When the residual stress of the top view and the side view(Figure) was measured by XRD, the...
10 January 2023 3,373 4 View
What is the meaning of the C/O ratio in XPS analysis? For example, Sample 1 's C/O ratio is 3 and Sample 2 's C/O ratio is 4. then, What can I get from this difference?
07 June 2022 4,183 2 View
AlSi10Mg powder was made by gas-atomizing. and this powder has poor flowability. so, I tried to dry the AlSi10Mg powder on vacuum, but it doesn't work. How can I improve flowability AlSi10Mg...
11 April 2022 8,890 5 View
I am planning to measuring residual stress using Nanoindentation. And I need the stress-free sample for reference. The sample that I want to measure is AlSi10Mg , makes Additive...
11 March 2022 9,789 3 View