Why discontinuous yielding occurs?

The relation of discontinuous yielding with micro-structure of low plain Carbon steel

14 March 2020 655 4 View

What kind of microstructure of Low Carbon Steel favors the maximum yield stress (>400 MPa)?

Micro-structural effect to Yield stress and yield ratio of low carbon steel.

14 March 2020 4,103 2 View

Is it possible to increase the yield point of a Low Carbon(0.22%) Low Alloy steel from 320 MPa to 400 MPa by hot working? How or Why?

Low carbon low allow steel usually show low yield ratio. I want to investigate the reason behind this.

12 March 2020 7,115 2 View

What are the possible reasons behind the low yield strength (320 MPa) and high UTS (630 MPa) of a steel bar?

Composition of the steel: C-0.22%, Mn-1.22%, Si-0.21%, P-0.032%, S-0.022% Cr-trace, Ni-trace, Cu-trace. In tensile test Elongation was around 18%. YS- 320 MPa, UTS-630 MPa. Microstructure of the...

11 March 2020 8,945 1 View

Prediction of the reasons behind low yield ratio from micro structures and chemical composition of low carbon steel.

Composition of the steel: C-0.22%, Mn-1.22%, Si-0.21%, P-0.032%, S-0.022% Cr-trace, Ni-trace, Cu-trace. In tensile test Elongation was around 18%. YS- 320 MPa, UTS-630 MPa The possible reasons...