when we scan the electrochemical behavior of a mof its redox peaks are visible but when they make a composite with some material like Polyoxometalate, then in cyclic voltammogram of this composite only the peaks of material other than mof are present. why the peaks of mof disappears in presence of other moiety?
Aamir Hassan Shah
Dear waqas, It will be better if you attach the voltammogram of MOF as well as POM based MOF. There maybe several reasons e.g. change in redox potential because of electron donation or subtraction effect, Peak overlapping, and third and major reason maybe the POM BASED MOF redox potentials may not be in the potential window you are using