Which type of transition temperature are you talking about? Melting or glass transition? Which polymer do you use in your work?

If the polymer is highly cross-linked, it won't crystallize at all since the crosslinking density is too high, preventing the crystalization of the polymer chains.

 Dear Thomas,

I am talking about glass transition temperature, It is a typical polyurethane system. I am thankful for your reply.