What would be reason, if tensile strength and elongation both increases in polymer composite?

10 October 2018 1 2K Report

It is known that if strength increases, elongation will decrease in natural fiber composite. What can be the explanation if we observed increase in strength and elongation both?

Souvik Chakraborty

The stiffness as well as the dutility (of sorts) is increasing. Monitoring the structure of the fibres and/or visible necking while testing can help get some answers.

Badges
Science topic

More Yogesh Marathe's questions See All

How can I remove NaCl from water soluble compound?

I have tried to remove NaCl using dialysis. It is working but it takes a long time. Is there any alternative method for this?

08 September 2016 5,692 6 View

How to measure a percentage conversion of monomer to polymer?

Curious to learn how much conc. of monomers are converting into polymer

05 June 2013 7,275 14 View

flexibility of polymers chain

effect of double bond on the flexibility of polymers

07 April 2021 0 0 View

Formulation of polymer color flakes

I am writing to request some information for making polymer color flakes. I would appreciate the help.

17 March 2021 0 0 View

Polymer composites suddenly solidifies?

I am making polymer composite by solvent mixing method. When I am trying to add filler solution in polymer solution it quickly get solidified. How to make them then uinform? It doesn't give time...

03 March 2021 7,540 4 View

What techniques can I use to determine the miscibility of polymer blends?

The term miscibility refers to the single-phase state in thermodynamics. I do not mean the compatibility of different components. To determine the miscibility I know several techniques such as...

03 March 2021 4,107 4 View

Resistor definition in Piezoelectric bimorph with ANSYS workbench

Hello, good day! I am trying to simulate similar bimorph piezoelectric harvester with below commands. However, the output power doesn't change with resistor value. Please help to find the reason. ET,10,CIRCU94,0 !SET UP RESISTOR R,1,100000 !RESISTANCE VALUE TYPE,10 !SET ELEMENT TYPE E,1,2 !CREATE RESISTOR BETWEEN NODES 1 AND 2 Thanks in advance Regards,

02 March 2021 0 0 View

Where can I find life cycle inventory or assessment of non woven materials?

Dear network, I am looking for the LCA or LCI or at least the energy balances of the non woven fabrics process for my master project, in specific for natural fibers, yet I have found...

02 March 2021 9,662 1 View

New Journal, "Integrative Psychological and Behavioral Science" -- do you not know, and have you not seen, this done before?

Question to you and THEM, the New Journal, "Integrative Psychological and Behavioral Science" -- do you not know, and have you not seen, this done before? There appears to be a core problem for...

02 March 2021 3,024 2 View

Joint behaviour in Abaqus is not captured well?

I am working on roof joint and trying to simulate the behaviour in Abaqus. I am successful in running the model but the final graph does not follow the experimental curve in the negative direction...

01 March 2021 6,661 3 View

Does any one can help me choose a reasonable basis set for intermediate metal ions interactions with guanine (i.e Fe2+, Mn2+, Cu2+ and exc.)?

Hello every body Does any one has any idea to help me choose a reasonable basis set for intermediate metal ions (i.e Fe2+, Mn2+, Cu2+ and exc.) interactions with guanine or other DNA organic...

01 March 2021 6,187 2 View

Glass fiber content in a gypsum board ?

Any idea on how to get the volumic ratio of glass fiber in a gypsum board ? Thank you for your help !

01 March 2021 2,501 3 View