I electropolymerize L- Valine on GCE electrode from 10mM L-Valine solution within potential range of -1.0 to +2.0 at scan rate 50 mV/S in 0.1M PBS by applying 12 consecutive CV cycle. All standard paper used scan rate of 100mV/S . But at 10mM concentration my CHI660 workstation don't support 100mV/S scan rate , at that condition it display 2 CV that looks like standing wave . How to solve this ? Is there any problem in the property or thickness of polymer film if i use 50 mV/S scan rate instead of 100 mV/S ? Is the number of CV cycle needed to be changed scan rate of 50mv/s ?