What can be inferred if the area under CV curve of a supercapacitor decreases as the content of nanoparticles increses??

H. T. Rahal @H-Rahal-2

15 March 2016 1 8K Report

cyclic voltammetry

supercapacitors

area under CV

nanoparticles content

Sridhar Srinivasan

Dear Hanan,

Can you explain your query with little explanation??? if possible,can you provide the numerical value of Area you obtained before and after increasing nanoparticle content and the mass of loaded nanoparticles???

Is it the area or capacitance that decreases with increasing nanoparticle content???

Badges
Science topic

Similar topics
Papers

More H. T. Rahal's questions See All

Do you think can be any Uranium bearing rocks in Eastern part of Iran and western part of Afghanistan?

I want to know more about Uranium ore deposits in world.

11 August 2024 6,720 0 View

Do you think can be any diamond bearing rocks in Eastern part of Iran and western part of Afghanistan?

I want to know more about diamond ore deposits in world.

11 August 2024 2,167 1 View

What is the difference between mathematical R^4 space and physical 4D unit space?

We assume that the difference is huge and that it is not possible to compare the two spaces. The R^4 mathematical space considers time as an external controller and the space itself is immobile in...

10 August 2024 6,678 14 View

If Banks do not provide credit facility, what are the options available for FPOs and impact on producer’s income?

10 August 2024 8,198 5 View

Controlling for pupil light reflex when analyzing pupil size time course?

I used eye tracking to examine how participants from two different populations (A and B) react to an image. Participants in population A exhibit larger pupil sizes over time, but they also have...

10 August 2024 3,229 0 View

What are a “Farmers Producer Organization” (FPO) and its essential features?

10 August 2024 477 5 View

Strugglling with m6A dot blot any suugesstion ?

I have been doing the m6A dot blot for a while with no improvement, I am extracting the RNA, and I can see the dots although the three biological replicas give a different reading on the memberan...

10 August 2024 8,539 5 View

Do interactions between biosphere, carbon cycle, & water cycle impact global warming & interaction between atmosphere & hydrosphere?

How do interactions between the biosphere, the carbon cycle, and the water cycle impact global warming and interaction between the atmosphere and the hydrosphere?

09 August 2024 3,291 2 View

How to get moment output in Abaqus Standart?

I have input a moment load in module load Abaqus, i put my moment load on the node surface (using reference point). I have define moment in history output and make a set for moment too. But the...

08 August 2024 4,831 4 View

How is energy cycled through the Earth's climate system and how do matter cycle and energy flow through the rock cycle?

08 August 2024 8,162 0 View

How to determine the charge passing during a cyclic voltammetry?

Dear All, here is my question: if I have a 15-scans cyclic voltammetry performed with PalmSens, how can I obtain the charge passed during the process? Hopefully avoiding integrations,...

29 July 2024 3,733 5 View

Why semicircle of nyquist plot is not complete?

While I am doing HER, I noticed that nyquist plots of Electrochemical Impedance Spectroscopy (EIS) is not complete. Will it affect for the Linear Sweep Voltametry (LSV) data? However, I can found...

26 July 2024 7,542 4 View

What binder would be the best choice to modify glassy carbon electrode with a 2D Material like Graphene or MXene?

I am trying to drop cast 2D Materials on Glassy Carbon Electrode for Cyclic voltametry and EIS purpose. What would be best binders to use?

23 July 2024 5,776 2 View

Can you please help me with a cyclic voltammetry?

Hi, I was wondering if you could help. When I take CV in GC electrode with the solution of InCl3 0.01M + citric acid 0.01M + NaCl 0.1M, I get such a graph, how can I correct it so that the...

11 July 2024 5,024 1 View

My Cyclic voltammetry curve doesn't show cathodic peak of Cu2+ to Cu+. how to solve this problem?

I performed CV of Cu-MOF in a buffer solution of pH 8, and we did not find any peak corresponding to Cu2+ to Cu+. What is the reason behind this? Please give your valuable suggestions.

08 July 2024 2,388 4 View

Does the specific capacitance value decrease or increase over time?

Will these measurement results change, for example, 1 month after the first measurement (e.g. CV, EIS) of the electrode or supercapacitor device? If it changes, how will it change? Is there an...

03 July 2024 3,644 2 View

How to identify if a material is behaving like an anode or a cathode?

when we perform a cyclic voltammetry study, how can we conclude if a particular material is behaving like an anode or cathode with the help of that CV plot?

20 June 2024 1,453 3 View

Knowing the CIF file No?

I am working on metal-organic framework for supercapacitor application. so, i want know about the Bi-trimesic acid CIF file number and Cerium also

09 June 2024 3,877 0 View

What amount is good for making an electrodes in supercapacitors? Many of the authors used 0.5 mg and other used more than that why?

Is there any advantage/disadvantage for choosing less amount (i.e., 0.5 mg) Or in choosing higher amount (1 or 2 mg) ?

06 June 2024 6,938 2 View

About potential window in supercapacitor asymmetric device?

If the electrode material in 3 electrode system, exhibit potential window only in the negative region, for the material how to choose potential window in asymmetric device

29 May 2024 861 1 View