There is a lot of factors for successful doping of an element on the solid support. Especially your method is very important. The other factors are the type of your precursor, reduction agent, loading amount, the charge of the precursor, solubility of the precursor, temperature, the interaction between support and precursor, etc. If you use gas or pressure system, also the pressure of the system is an important factor.
a lot of factors such as reduction agent, loading amount, the charge of the precursor, solubility of the precursor, temperature, and .......
There are so many factors.
Few articles about that:
https://www.researchgate.net/publication/311977968_Accelerated_formation_of_BaTiO3_ceramics_with_mechanochemical_processing_in_different_liquids
https://www.researchgate.net/publication/267251207_Synthesis_of_Nano-sized_Barium_Titanate_Powder_by_Solid-state_Reaction_between_Barium_Carbonate_and_Titania?ev=pubitem-pub_cit&_iepl%5BviewId%5D=FuqiKDlj8hLwehR1ocK8W11Vd2xqVoTlxtE2&_iepl%5Bcontexts%5D%5B0%5D=pdppi&_iepl%5Bdata%5D%5Bmilestone%5D=experimentMilestoneClickedToPublicationFromCitationWithFulltext&_iepl%5BinteractionType%5D=publicationView
https://www.researchgate.net/publication/305729376_Effects_of_Ultrasonication_and_Conventional_Mechanical_Homogenization_Processes_on_the_Structures_and_Dielectric_Properties_of_BaTiO3_Ceramics
https://www.researchgate.net/publication/270464788_Mechanical-Chemical_Synthesis_Ba077Sr023TiO3
https://www.researchgate.net/publication/248454348_BST_ceramics_Effect_of_attrition_milling_on_dielectric_properties
https://www.researchgate.net/publication/233358548_Correlation_Between_Densification_Rate_and_Microstructure_Evolution_of_Mechanically_Activated_BaTiO3?ev=pubitem-pub_cit
Article Accelerated formation of BaTiO3 ceramics with mechanochemica...
Article Synthesis of Nano-sized Barium Titanate Powder by Solid-stat...
Article Effects of Ultrasonication and Conventional Mechanical Homog...
Article Mechanical-Chemical Synthesis Ba0.77Sr0.23TiO3
Article BST ceramics: Effect of attrition milling on dielectric properties
Article Correlation Between Densification Rate and Microstructure Ev...