There are several dispersions for electrodeposition available. The question is: what hardening and what crosslinking mechanism you would like to use. After depositing a certain film-thickness you have to dry it in an oven. Electrodepsition-coatings for cars are normaly crosslinked with melamine 30' 140°C, but binders for UV-hardening are also available.
Thanks for reply. I am callow & planning to remove organic effluents by coating nanoparticles on electrodes & pass current. I have synthesized nanoparticles & they are good. Now i have to coat them on titanium mesh so that they dont get peel under effluent treatment.
What type of binder can be used for it? I am new to this field & i require your guidance so please help me.