Hi

I synthesized NiCoFe2O4 nanoferrite. I used XRD to prove the formation of NiCoFe2O4 nanoparticles. I understood that the position of the peaks is correct. I mean that the nanoferrite powder diffracted in correct angels (2 theta = 35, 40, 43, 65 degree) based on references but MY PROBLEM is the sharpest peak in references is in 35 degree but my sharpest peak is in 43 degree. (I have the most count in 43 degree but in references the most count is in 35 degree). Is it important or no? and could I claim that I synthesized NiCoFe2O4 nanoparticles successfully? If not, how can I prove that?

I`d be thankful if help me.