Is there any lowest possible level of dilution region above the interface by PTAW by controlling process parameters?

11 November 2015 1 4K Report

For base metal of 316 L SS and hard facing alloy of colmonoy, is there any lowest possible level of dilution region above the interface by PTAW by controlling process parameters? For Eg. 600 or 700 micron above the interface

Babu Bhaskaran

Refer this link:www.arcraftplasma.com/welding/PTWA.pdf

Refer this link:www.tandfonline.com/doi/pdf/10.1080/15560350802316744

Refer this link:iosrjournals.org/iosr-jmce/papers/ICAET-2014/me/volume.../17.pdf?...

Badges
Science topic

Is there a good macro photography kit for on-site metallurgical investigation?

I am looking to purchase a photography kit for onsite metallurgical investigations, such as capturing photos of worn areas, hot tears, cold tears etc. Could anyone suggest me a good...

22 July 2024 3,490 2 View

What could be the possible reason that sintering of polycrystalline diamond fabricated with tape casting has suddenly started failing?

I make polycrystalline diamond with tape casting followed by HPHT sintering. When i sintered the samples up till May, the sintering was good. When i sintered the samples in June and July at the...

16 July 2024 3,212 5 View

What binders suggestion that I can use for zinc alloy?

I am working on powder metallurgy, and during the compaction process, the powder does not pelletize and remains in its powder form. To address this issue, I am considering using binders to improve...

13 July 2024 9,003 2 View

What may cause whitish discolor of polycrystalline diamond surface, and cracks near edge?

I am preparing polycrystalline diamond (PCD) with tape casting. The powder is 8~12 um. After drying of tapes, I place several tapes in Ta cup without warm-pressing. Next, debinding is carried...

23 June 2024 7,758 2 View

How do we interpret the origin statement ?

Crystallography Doubt_International Table of Crystallography In the space-group number 185 of ITA (see Attachment), how do we interpret the origin statement?

08 May 2024 10,055 0 View

Why stainless steel is not attractive to magnetic feild?

In material science, steel have more group, So what is the best explain answer according in metallurgy science?

21 March 2024 835 4 View

Phase Grain Contiguity & Bonding Phase Thickness of Powder Composite?

Hi. Can anyone explain to me these terms: 1) Phase grain contiguity 2) Bonding phase thickness Q: Simple explanation on this? How to measure this properties? Software / formula ? How does this...

03 December 2023 4,823 1 View

What mechanical tests are important for magnesium scaffolds that have a high percentage of porosity and are produced by powder metallurgy?

What mechanical tests are important for magnesium scaffolds that have a high percentage of porosity and are produced by powder metallurgy? Does this include only compression tests? Can bending and...

21 October 2023 9,785 1 View

What viscosity Methyl cellulose binder is used for tape casting of 10 um powder particles? What are general recommendations for such sized particles?

I am using 4000 cP methyl cellulose for aqueous tape casting. Since it gives very viscous solution, I am dissolving it in 1.5 wt% in 98.5 wt% DI water. Still it is a very viscous solution. Because...

17 October 2023 1,919 2 View

What is the maximum Si content in Al-Si alloys and the parting limit during dealloying/chemical leaching?

We recently 3D printed (SLM) hypereutectic (high Si)% Al-Si-alloys and chemically removed the Al afterwards (via HCl (aq)) in order do get a porous structure, which worked quite well. 1.) I was...

16 October 2023 1,716 1 View