Hello,
I would like to have coatings that can be applied to surfaces (metal, PMMA, or glass) to obtain a contact angle with water greater than 110°.
I'm looking for either coatings or materials.
Thank you very much
If you want a native contact angle over 110 there are not a lot of choices. See thjs
https://www.accudynetest.com/polytable_03.html?sortby=contact_angle
or this
https://en.m.wikipedia.org/wiki/Contact_angle
we have a method that increases contact angle by ~50-60 degrees for most polymers
Article Photoreactive Superhydrophobic Organic-Inorganic Hybrid Mate...
Thank you :)
Hello, We know that measuring contact angle and surface energy is important in various industries, such as: cleaning, coatings, adhesives and surface treatment. Is it necessary to have a...
28 March 2024 5,880 2 View
Since we aim to define the integral of a mapping, we typically employ either the Riemann or Lebesgue approach, involving the computation of lower and upper sums. However, this assumes a total...
26 March 2024 1,145 0 View
How to measure concentration of colloidal silica in water. Does ICP-MS work and does it require colloidal silica dissolution beforehand ?
19 April 2017 4,460 1 View
How can I determine a good adhesion strength range for coatings on polymer surfaces, such as DLC on polymer substrates? Is there a specific threshold for adhesion strength (from T-peel tests)...
10 August 2024 942 3 View
I need a very narrow glass capillary for my research. How can I make a glass capillary with an inner diameter of around 200 to 500 nanometers?
08 August 2024 8,915 0 View
I have been using Gromacs 2021.7. I wanted to simulate two small molecules in water. But, while generating the ions.tpr, I am getting the following error. The topol.top and .itp files for each...
17 July 2024 9,897 4 View
As, my studies are related to water adsorption, the substrates should be hydrophilic in nature. Ni-foam being hydrophobic in nature, the results are not as expected as in literature. Hence i...
14 July 2024 8,847 4 View
I will polymerise Aniline on ITO glass WE, using 1M of H2SO4 and a potentiostat. However, I am not sure if I have to do the electrochemical polymerisation inside a hood. Is it necessary? Is the...
10 July 2024 2,937 3 View
Hi all, I am looking glass cilinders that have an open flat bottom and top. Preferably with the inner diameter in the range of 2 cm. It's similar to the ones found on multi-electrode arrays for...
06 July 2024 5,846 1 View
If we want to introduce a material similar to polymethyl methacrylate "with the characteristics mentioned in the next paragraph" that can be added to a precursor and create a composite, which...
03 July 2024 2,371 1 View
I use PDMS to build a microfluidic system, but it is not hardening at all, although I use TEOS as a cross-linker and also ATPES in a ratio of 1:10, and it's been 3 days at 80 degrees of 3 ml cast...
01 July 2024 604 3 View
To prepare polymethyl methacrylate polymer for the study of acoustic properties, a mixture of methyl methacrylate monomer and benzoyl peroxide is used. This mixture is then heated and placed on a...
27 June 2024 2,087 1 View
Is direct contact of polllutant and catalyst needed? or indirect contact just like photocatalyst wrapped inside glass can also create hydroxyl radicals and elimnate pollutants near to its wrapped...
23 June 2024 3,249 5 View