I am currently delving into the application of the ParaDis Dislocation Dynamics Code. Multiple DD simulation papers suggest that the initial dislocation data involves distributing frank-reed sources across all available slip systems. In ParaDis, the creation of Initial Dislocation Data relies on Paradisgen. However, I'm encountering difficulty locating an option to distribute frank-reed sources across multiple slip systems for FCC materials. Seeking guidance from those familiar with this process. Your insights would be immensely appreciated.