One of our silicon masters was accidentally broken while casting in pdms. Getting replacement is not an option at this time. Could you please suggest a way in which we can fix the master such that it can be used again for casting.
I would suggest using the last casting to create a copy of the master in another material like epoxy or casting resin. You could even use PDMS to make a flexible master.