Hi everyone,
i am calculating capacitive and diffusive control charge storage behavior of MnOx and i have problem that when i calculate just capacitive behavior its curve crosses at certain voltage and also go outside the main curve . is there anyone to help me out in this regard. i am attaching CV in attachment
I had the same question as you until I figured out the "secret" late last year:
The differentiation method that you have practiced is not a general method and needs to fulfill the requirement: no discernible peak shift or CV shape distortion should be observed. Both of your CV curves are highly distorted. In addition, the method is invalid for potentials close to two limits. I usually stop at potentials that are 0.3 V aside the two boundaries.
I've also attached my slides dealing with this issue for your reference.
thanks Tianyu,
i have download your slide and started reading your slides but there are some slides missing like of step i 2 3 4 if you please provide me your slides i will be better able to understand this method
and secondly shall i used Dunn method or Trassati?
thanks