Graphitization of the carbonized materials
1.0 g of the carbonized materials and 0.5 g FeCl3.6H2O were added to 100 mL distilled water. In addition, the pH of the solution was adjusted 2 by adding HCl. The mixture was stirred at 60 C for 5 h, then left for one week for gradual evaporation of water at room temperature, and finally dried at 100 C for 5 h to achieve a black solid material. Can anyone help with the mechanism it undergoes?
As, I understand your problem, the carbonized material undergoes dehydration, polymerization, atomization and then nucleation which results in formation on black solid material.
Sir,
It's a general mechanism by which bulk carbon undergoes nucleation and turns into nano carbon form
The soot formation and characterization have received considerable attention over the past years from research activities in the field of combustion and pyrolysis of fuels .Due to the effect of temperature and its time variation on the extent of carbonization of soot, variation in soot nanostructure and soot oxidation rate is known. Differences in the soot growth mechanism, caused by different soot growth species formed during the fuel decomposition may also lead to differences in structure. The formation of graphite results from the elimination of defects at heat treatment.
In general, the soot formation is not yet fully understood. Some studies have suggested that the soot formation may be formed by following four main steps:
-nucleation of young soot particles
- particle coagulation
- particle surface growth and oxidation
- particle agglomeration.