Certanly silane layer will suffer. Strong particles grinding will take place in a ball mill or planetary mill. I only could suggest you alumina colloidal grinding in silane solvent and only after that drying in oven. It will help to form new sliane layer as grinded surface generated, which decrease agglomeration