The formation WC, which acts as second phase particles in Co-Cr matrix , and then hinders the motions dislocations as well as the grain boundary migration. The result is the increase in the strength of the alloys according to the connection: SigmaY= Sigmao + 4G b/ Lm where Lmis the mean distance between dispersed particles.
Compressive strength of Co-Cr alloys increases upon addition of tungsten. Co-Cr-W alloys are ternaries first investigated by Haynes. He discovered the high strength and strainless nature of binary Co_Cr alloys. Later by adding Tungsten as powerful strengthening agent within the Co_Cr system, which is also called Stellite alloys in practice..