Dear Gopikrishna

This is dependent on the coating.   If the coated material is ductile, i.e., organic coating, the composite of the coating/substrate might becomes high graded ductile materials.   In contrast,  If the coated material is brittle, i.e., inorganic  coating like a ceramic, the composite of the coating/substrate might not becomes high graded ductile materials under particular loading modes.