Can we remove impurity peaks or stabilize the phase by recalibration?

13 January 2024 1 8K Report

I'm currently working on LLZO and I'm getting little impurity peaks in xrd. So is it possible that by recalcination we can remove those peaks?

Haobam Samananda Singh

Dear friend Manish Kumar the peaks corresponding to xrd peaks can be removed by recalcination at different temperatures. However, the problem is why the peaks come out.

If the peaks come out due to an incomplete reaction during calcination, then peaks will be removed. If not, you have to search for the reason behind the peaks. And that will be the beauty of the research.

Badges
Science topic

Similar topics
Filing

More Manish Kumar's questions See All

What is the relationship between the threshold voltage and the device's noise performance, particularly in terms of flicker noise and thermal noise?

The threshold voltage (Vth) of a MOS device plays a crucial role for its operation. At the same time, noise is an intrinsic factor. So how noise (flicker or thermal) change with the change in...

29 July 2024 3,244 0 View

What is the solvent system required to run tlc for calixarenes?

If you don't understand my question let me know

21 July 2024 561 1 View

Sample size for qualitative study?

I am working on scale development in behavioral finance by undertaking a mixed-method approach using the exploratory sequential design. The phenomenon has diverse meanings in existing literature...

20 July 2024 9,150 11 View

How to convert available phosphorus to total phosphorus?

I need to convert Available phosphorus into total phosphorus

18 July 2024 6,797 3 View

Can it is possible to find the cleaved sequence when a protein cleaved by a heamaglutanin protease (HA/P) by any bioinformatics tools?

Bioinformatics tools like peptide cutter

15 July 2024 6,453 1 View

Can we progress towards defining obesity based on body fat content?

The burden of obesity is enormous. The greater challenge lies in accurately diagnosing obesity at the right time, reflecting the true increase in visceral fat. BMI may not accurately represent...

14 July 2024 8,768 4 View

How can I do photodetector application from Inorganic nanoparticles compound?

I have an inorganic nanoparticle compound I want to do a photodetector application from this compound, I do not have any idea, can anyone help me with this?

11 July 2024 135 1 View

How does high humidity affect the growth and development of crops?

10 July 2024 7,256 20 View

In what ways does high humidity impact the pollination process in agricultural plants?

10 July 2024 7,513 13 View

Do the parts of the body that are situated at a longer distance from the central nervous system have the least control & coordination comparatively?

What would be the effect of distance from CNC cum Heart on the structure and function of a particular part of the human body? Do short people have evolutionary advantages to control body parts in...

09 July 2024 2,050 3 View

Melt curve problem in qPCR?

Do these peaks in the curve indicate primer dimer or non-specific products?

01 August 2024 7,465 0 View

How to improve peaks separation in HPLC?

Hi everyone, I'd like to better separate two close peaks coming from a bioconversion sample, I'm currently using a C18 KromaPhase 4,6mm Ø.I. SCHARLAU, particle size (µm): 10, pore size (Å): 100,...

30 July 2024 433 3 View

What does an additional peak in FTIR between 3100 and 3300 nm affect the quality of the material, benzethonium chloride USP??

I do not know much about FTIR! The material Benzethonium Chloride USP was compared to a reference standard in regards to FTIR, as per the USP testing: Identification B. Infrared absorption (FTIR),...

16 July 2024 6,916 7 View

Validated HPLC method for the estimation of the Amphotericin B ?

During the release test of Amphotericin B using 1% Tween 80, i observed three peaks even in the standard. The first peak consistently yielded results around 500%, while the other peaks showed...

08 July 2024 1,329 0 View

Why there are no peaks at downfield NMR of Cobalt and Nickel complexes?

I synthesized some paramagnetic cobalt and nickel complexes (expected to be Co(II) and Ni(II)) using a bidentate ligand - N of pyridine ring (aromatic) and O of P=O (aliphatic), and I obtained...

03 July 2024 3,410 4 View

How can I put small FWHM in CasaXPS?

I'm trying to fitting Cu Auger peak into various state (Cu0, Cu+, CuI etc..) In Cu0, one of the peak's FWHM is 0.84 but when I try to enter smaller value than 0.89, "input error" is occured. How...

02 July 2024 4,932 3 View

What is the reason of appearance of 2 or 3 peaks in zeta potential analysis of sample?

Hello I have prepared metal nanoparticles and did zeta potential. Normally there is a single peak in sample but now there are 3 peaks. I prepared sample for analysis first I prepared 10 mg/mL...

30 June 2024 1,063 4 View

EDS or EDX concetration finder?

Hello everyone, I'm facing an issue with EDS software that prevents me from obtaining atomic or weight percentages for my scan. However, I do have access to the raw data, which shows intensity vs....

29 June 2024 6,663 14 View

Could you please help me to match the XRD peaks of MoVO oxides?

Hi all, I have few XRD files of MoVO oxides. These are newly synthesized compounds. Can anyone suggest me, how can check my XRD files from database? I want to match my XRD peak to the database. Is...

24 June 2024 6,448 3 View

What does an increase in intensity mean in GIXRD?

When I examined the GIXRD data obtained recently, I observed that the sample treated with O2 plasma on the Cu surface deposited on Si chips showed increased intensity compared to the sample...

19 June 2024 6,898 5 View