Yes! There is absolutely no difference to pure silicon wafers. The reason: 100 nm is way too thin to "feel" any effect of a ductile metal in relation to the brittle silicion. Problems start when such films become thicker than ~ 5µm. (I did such things with Cu films on Si with thicknesses ranging from 100nm to 20µm)

Thank you very much. This helps me a lot!