Can anyone help me to calculate the d-space of this crystal structure?

More Magdy Ali's questions See All

How can one explain the Upconversion phenomena in nanomaterials?

We prepared CuInS nanomaterials. The nanoparticles were excited with 800nm and the yield emission peak found at about 700 nm. We can not find sharp explanation to this phenomena. Why this...

08 September 2018 4,646 0 View

What should I do if I submitted a manuscript to a journal, and the current status is "submitted to journal" for one 25 days?

What should I do if I submitted a manuscript to a journal, and the current status is "submitted to journal" for one 25 days? plus I received email from the journal informed me that they will give...

01 January 1970 9,821 30 View

Is it possible to plot the atom-projected band structure using GPAW?

Hi, I'm currently working on a project where I need to plot the atom-projected band structure using GPAW. I've been able to calculate the band structure for my material, but I'm having trouble...

07 August 2024 269 3 View

Absorption coefficient of methane?

Hello, Can anyone provide me with the absorption coefficient of methane gas at 7.7 um? Any reference?

06 August 2024 980 5 View

How to understand this crystallographic phenomenon of low temperature crystals in zeolite?

During low-temperature testing, new diffraction peaks that appear could be indicative of several phenomena. In one of our tests, we observed notable new peaks around 40° and 45° in a specific...

06 August 2024 726 3 View

How does one derive the standard deviation of a scale?

Dear all, I am working on analyzing data from a survey on student satisfaction. The survey contains items with a 7-point Likert response format that produce 12 scales related to different areas...

05 August 2024 2,141 4 View

How can I add own Henry coefficients in Aspen Plus?

Hi, i would like to simulate an absorption process in Aspen Plus. I want to use the NRTL model und would like to add some individual Henry coefficients. Is that possible and how?

05 August 2024 2,333 2 View

Why might the impedance values for DI water and 0.1X PBS buffer solution exhibit a decreasing and increasing trend, respectively over time (HP 4194A)?

Hello everyone, I'm encountering an issue with my electrochemical impedance spectroscopy (EIS) measurements and would appreciate some insights. Experimental Setup: Electrodes: Gold interdigitated...

05 August 2024 3,783 2 View

Why results of ROS flurescence are negative as there was no bacteria within?

Hello. I am working on ROS production of two systems: system A is cerium oxide and hydrogen peroxide, system B is cerium oxide nanoparticle, hydrogen peroxide and potassium bromide. I did some...

04 August 2024 5,974 3 View

Why is TLC not a form of partition chromatography?

Why is TLC not a form of partition chromatography and paper chromatography not a form of absorption chromatography?

03 August 2024 7,035 3 View

Mossbauer spectroscopy Co0.6Mn0.4Fe2O4 MNPs?

Following curve related to Co0.6Mn0.4Fe2O4 Magnetic nanoparticles with extra phase a-Fe2O3. I will appreciate to help me to interpretation this spectroscopy, especially the blue line.

31 July 2024 9,140 2 View

¿Are oxygen vacancies in semiconductors capable to change the band gap?

Dear all! Oxygen vacancies do raise negatively the Fermi level by increasing the negative charge in the semiconductor crystal structure. In the case of n-type semiconductors, I wonder if this...

30 July 2024 8,339 2 View

Baydaa Abdul-Hassan

Dear Magdy Ali,

This chapter may be useful for you as I hope,

Chapter 2

Size Effects on Semiconductor

Nanoparticles

Rolf Koole, Esther Groeneveld, Daniel Vanmaekelbergh,

Andries Meijerink and Celso de Mello Donegá

If you give me some more details about your material I may give you more help.

With all my best wishes.

Magdy Ali

Thank you so much,

my project is CuInS quantum dots.the attached photo is the SAED for crystal size of about 4nm

thank you again