Hello, I have researched almost ferromagnetism or antiferromagnetism. And I draw the experimental data after measurement using Origin lab such as M-H, M(Chai)-T, Cuire-Weiss law, Arrott-plot, etc I heard. Those are what I know and heard. So, if there is anything to analyze magnetic properties I didnt know ?
If there is, please let me know !
Thank you ~
Hello Kim,
Magnetism is a vast field, could you please share more further information. For example what kind of material are you analyzing and what is your objective.
Cheers
Amar
Thank you for replies. Lately I am determined to try to synthesize Gd compounds due to its large magnetocaloric effect. So, I'm wondering that there are other methods to analyze except for what I mentioned above. Also, I found Arrott-plot which shows what is the magnetic transition in materials; First order magnetic transition or Second order magnetic transition. Like this, I would like to know any special things to draw and analyze from M-H, M-T data or what I can measure.
I can measure M-H, M-T, heat capacity, resistivity, etc.
If it can't make sense, in brief, just I know kinds of the method to look up and analyze magnetic properties.
Thank you for reading ! Wait for replies.