I would like to know how to find a octahedra tilting angle and what program is best to do this. I have installed POTATO, Spuds. But problem I had with these programs is that there is no proper...
03 March 2014 7,169 3 View
While treating preferred orientation for powder data say using March-Dollase function, we need to find the plane which is affected from texture. As per my understanding suppose (022) reflection is...
02 February 2014 1,962 2 View
I would like to know if there is any tutorial available to perform multiphase refinement in GSAS. I did not find it in GSAS manual. I need to know the important strategies while refining two...
01 January 2014 7,004 9 View
I used GSAS/EXPGUI for refinement. Is there any possibility that I can use GSAS file and draw Fourier map in Full Prof?
09 September 2013 312 7 View
I need to do Rietveld refinement for synchrotron X Ray data which has thousands of profile points. Currently I am using GSAS/EXPGUI but it takes a longer time to converge. Will sequential GSAS...
05 May 2013 7,433 7 View
What is the meaning of negative scattering length in neutron diffraction? Ex: Vanadium has negative scattering length for neutrons.
03 March 2013 5,220 4 View