I cast a slab 50 cm x 50 cm x 9.5 cm slab with 12mm rebar spacing at 12.5 cm. When I apply the impressed current method to accelerate the corrosion (1A current). After the current method slab was...
30 September 2015 4,181 3 View
I am doing an experiment on corrosion in reinforced concrete. I am using half cell potential equipment and impressed current method to accelerate the corrosion. The factors I am considering for my...
04 July 2015 5,350 2 View
I am using half-cell potential to check the effect of cover depth, permeability and moisture content. How long do I have to pre-wet the surface?
25 February 2015 7,839 3 View
I am little bit confused about how to setup the impressed current circuit for one-way slab with more than 5 reinforcement bars! Can anyone explain to me how to use anode and cathode for this method?
22 February 2015 4,823 1 View
I am using a 750 mm x 750 mm x 200 mm slab with 12 mm rebar placed at every 150 mm. I am bit confused about how I can create an anode and cathode for this slab? And I am using impressed current as...
22 February 2015 7,575 4 View
Is there any standard to use for this ? How should I design the slab for 3-point bending test?
06 February 2015 4,369 1 View
I am doing research related to corrosion. I need to get the results of corrosion using half-cell potential and concrete resistivity measurements when the reinforcement mass loss around 5-10%.
18 December 2014 6,663 2 View
I am doing research related to corrosion. I am using the half-cell potential method and the concrete resistivity method. One of the factors I am considering is the effect of moisture content.
17 December 2014 7,321 2 View