What is bright region between crack growth and post tearing?

Dear All, We carry out fracture test of Zr alloys. To distinguish crack growth during fracture test, we carry out heat tinting at 300 oC for 20 min at no load and then samples are torn apart to...

16 June 2017 4,760 3 View

Is separation of J into elastic j nad plastic J correct?

As per ASTM-1820 J is separated in elastic J and plastic J. Elastic J is calculated as per eqn. Je=K^2*(1-v^2)/E and plastic J is calculated from area under load vs. plastic displacement. I want...

13 April 2017 3,694 19 View

How to model buckling of CT specimen?

I have carried out fracture toughness of Zr-2.5Nb pressure tube using CT specimens in transverse and longitudinal direction. The transverse CT specimens got buckled during fracture testing. I want...

27 March 2017 7,021 8 View

How to calculate buckling load of CT specimen?

I have carried out fracture test of Zr-2.5Nb pressure tube material in axial (crack growth along axial direction of the tube) and transverse direction of the pressure tube using CT specimen. The...

10 March 2017 9,210 4 View

How to calculate slope of blunting line from stretched zone width?

As per ASTM E-1820 for J-R curve, slope of blunting line is given by: J=2sf*deltaa. But this blunting line equation may not be true for all material. It is said the stretched zone width is...

27 December 2016 8,526 8 View

What is minimum and maximum limit of a/W to be used for calculating eta factor experimentally and numerically?

I am calculating eta factor for 17 wide mm flat CT, axial curved CT and transverse curved CT specimens for fracture toughness testing of Indian Zr-2.5Nb pressure tube material experimentally...

14 October 2016 5,241 6 View

Which radius of a cylinder should be used to calculate folias factor for axial crack in a cylinder?

I want to calculate the critical crack length for axial crack in a cylinder based on fracture toughness. For that I need to calculate folias factor. I want to know which radius I should use to...

29 October 2014 9,753 1 View

Side grooving in fracture specimens

ASTM E-1820 recommend side grooving after fatigue pre-cracking. But I think side grooving before fatigue pre-cracking is better because the fatigue pre-crack front will be more uniform. Also,...