Your question is not very clear to understand. Please provide more information, especially on the shortcuts you are using (HCA, SBF). Please also, attach XRD data.

But If I understand correctly, you got some product that should not be present before some step?

If it’s a glass you’d don’t expect sharp peaks in the XRD analysis. Perhaps a single very broad peak.

Yes , i will get products such as wollastonite and etc . I attached XRD Data of material .

Dear Seyed,

thanks for attaching XRD data. It is composed mostly of amorphous material (bioglass) and some crystalline phase - maybe the wollastonite you proposed formed in the process of thermal treatment. But your question is still not clear.

I checked for shortcuts - HCA = hydroxycitric acid, SBF - simulated body fluid?

In these patterns you identified Bragg peaks for HCA?

Dear Michal,

Thanks so much

HCA : Hydroxy carbonated apatite.

HCA peak , was Identified in XRD pattern .

Hello

you can use xpert software.