My intention is to study the stability of compounds made up of Li, Al, Ge and P with different compositions. For this purpose, I need to plot a quaternary phase diagram, but I couldn’t find suitable software. So would you please suggest me a software which could be used for this work. Preferable if it is free.
Thank you in advance for your cooperation
Johan Zietsman
You can use FactSage for this. You will have to plot pseudo-ternary diagrams, since it is not possible to plot 4D diagram including 3 composition variables and temperature.
It ould also be possible, but difficult, to plot isothermal quarternary sections with 3D modelling software like Blender. The sections would be tetrahedrons.