Why recovery of Ca is different with CaSi, CaFe, Pure Ca Solid wire, Pure Ca powder wire?

29 August 2017 1 2K Report

Why it is said that pure calcium solid wire will give better recovery then CaFe wire or pure Ca powder wire?

Dear Somnath,

Factors to be taken into account are the help given to calcium solubility by diffrent alelemnts accompanying calciumand how the powder is shielded by the steel tube. A supply of pure Ca (so called HiCal) uses a special shielding that protects early melting of the calcium, thus giving higher calcium yield, but with a higher cost material

Badges
Science topic

More Somnath Kumar's questions See All

Which is the most efficient etching solution for nickel based alloys?

Which solution reveals the microstructure and features of nickel-based alloys?

02 March 2021 2,221 3 View

Which is the most convenient manufacturing software for Additive Manufacturing?

Which tools can be used to generate machine codes for additive manufacturing?

02 March 2021 7,220 2 View

Which is the best place in the world for the plant biotechnology research?

I am searching for a good place for the Post Doc,

02 March 2021 4,053 3 View

Which SAR dataset to use for generating coherency matrix and performing target decomposition (Description) ?

Working on chandrayaan-2 DFSAR data, there are three datasets available: 1) Slant range image data product: The slant range complex image file. Each pixel is represented by two 4-byte floating...

02 March 2021 8,481 3 View

How does one access the Cranet survey data on HRM practices?

Hello, The Cranet website does not provide any lead to the data obtained from their multinational survey on HRM practices. Any help on accessing the data would be most appreciated. Thank...

01 March 2021 9,536 3 View

Genome-wide gene identification protocol ?

Is there any book chapter/book, webpage or research article available to understand genome-wide gene identification?

28 February 2021 8,095 1 View

Can the problems of overfitting be solved without cross validation?

For an overfit data set the cross validation error will be much bigger than the training error. Is it true or false?

23 February 2021 3,616 2 View

Research Gate Does it help researches to publicize their scientific work ?

In my opinion, the RG site is useful in solving scientific problems and shows the researcher's ability. Besides, the separation of the H-index from the self-citations and the overall index is an...

22 February 2021 3,894 6 View

How to Study a proton NMR of Graphene prepared by Electrochemical Exfoliation technique?

I performed a Proton NMR of graphene powder prepared by electrochemical exfoliation technique. It shows some peaks. But I can't understand it.

21 February 2021 8,947 3 View

How to classify and recognize unseen image class in document sorting?

To sort the scanned document image I have to determine the class of document. But no of classes of image will keep on adding even after training. So at time of inference first I will detect unseen...

16 February 2021 4,501 3 View

What is the status of bread making and more bakery foods with the use of insect flour/powder?

Insects have been consumed by human diet since prehistoric times. At present, the idea of looking at insects as food has been getting traction worldwide, also in response to increasing food...

03 March 2021 6,223 5 View

What is the production process of CaFe ferroalloys?

I looking for ferro calcium production process

03 March 2021 1,755 4 View

Sutter electrode holder leaking after applying positive pressure. How to fix?

I am using a Sutter electrode holder for my patch clamp experiments, but I'm having trouble keeping positive pressure inside my electrode due to a leak out of the back of the holder. I have added...

02 March 2021 5,829 1 View

How to grow E.coli on the low salt LB agar plate with 50 or 100ug/ml of Blasticidin?

Hello, I would like to ask how to grow E.coli which resists 50 or 100ug/ml of Blasticidin. I have tried many methods by using low salt Luria-Bertain(LB) agar plate. However, no colonies grow. Let...

01 March 2021 2,027 2 View

Gas sensor response and recovery time independant of flow rate and chamber volume?

I am trying to obtain the response and recovery times for my gas sensor device. It appears the the response/recovery times are primarily dependant on the flow rate of the gas I inject into the...

26 February 2021 1,511 3 View

Have anyone checked before Cyclic voltammograms of intial ITO substrate and E-teck?

As a beginner in electrochemistry, I tried to obtain cyclic voltamograms of commercial anatase powder deposited on an ITO substrate or on Eteck. After several attempts, I noticed that my cyclic...

23 February 2021 3,175 3 View

How to reduce static electricity of powder after lyophilization?

I am working on synthesizing and then purifying peptides using the SPPS system. After purification of the peptide, the peptide powder is obtained using a freeze dryer. When measuring the powder,...

22 February 2021 10,099 5 View

What kind of steel moulds are used for hot pressing metal powders?

My main concern is that the metal powders should not weld to the mold surface and I should easily be able to eject out the pressed samples. I am looking for alternative for graphite moulds. The...

22 February 2021 2,965 4 View

Helix antenna coupling problem?

Dealing with a helix antenna, made with flexible material and not rigid like using a PCB board or wire. At the beginning of the helix is too close to the ground plane, causing coupling. How can I...

21 February 2021 4,453 3 View

How to Study a proton NMR of Graphene prepared by Electrochemical Exfoliation technique?

I performed a Proton NMR of graphene powder prepared by electrochemical exfoliation technique. It shows some peaks. But I can't understand it.

21 February 2021 8,947 3 View