I am looking for an alternative analysis or characterization to confirm my catalyst is a nano-catalyst other than TEM. I really appreciate any help you can provide.
Nano-sized samples can have higher bandgap also, so could be characterized with UV-Vis-NIR spectroscopy. As the surface area is much higher, can be probed via BET.