Other than single relaxation time how Debye type behaviour effects the electrical properties of amorphous semiconductors particularly chalcogenide glasses?
Sigma(omega) is not Debye-type in amorphous semiconductors, but rather power-law dependent. You can interpret this behavior as the existence of a distribution of relaxation times embedded in the Debye-type relation.