I try to degradation of natural rubber latex using 20% low ammonia NR latex.

"Degradation of NR was carried out by preparing latex with 20% dry rubber content (DRC). The pH of the latex was adjusted using formic acid to obtain the required pH (pH 5–9). Under continuous stirring, the mixture was heated to 70 °C before hydrogen peroxide and sodium nitrite were added simultaneously. The latex was then coagulated using methanol and filtered. The LNR obtained was washed four times with distilled water and dried in a vacuum oven at 60 °C."

; Polymers 2014, 6, 2928-2941; doi:10.3390/polym6122928

When I slowly added formic acid to control pH, the liquid latex was coagulated. How can I experiment while maintaining a latex state?