I want to manipulate the grain size of a kind of ceramic powder. My preliminary strategy is to extend the heat treatment time from 1 hour to 16 hours, hoping to get various grain size. Do you think it is possible? Or is there a better idea?
According to kinetics, time and temperature are two factors that affect the grain growth. But increasing temperature is much more effective than increasing time.
According to kinetics, time and temperature are two factors that affect the grain growth. But increasing temperature is much more effective than increasing time.
Increasing temperature is more effective than increasing time get larger grain size in sintered samples. Initial size and distribution is also important in predicting the final size after sintering. To control the grain size various additions can be made to the starting powder to control the grain size at a particular sintering temperature.