I want to simulate the diffusion bonding process of glass (Mechanial, not in atomic level) in ABAQUS. Basically I want to measure the bonding strength of these two bonded glasses at the interface. I've looked into literature, but I haven't found any existing simulation method. Could you please help me with any input?
Daniel Swiler
To answer your question, if temperature is high enough for interdiffuson it will be the strength of the intermediate glass. If the glass does not interdiffuse, it would likely mean that there is little bonding and a much lower strength.
You would need to know temperatures, surface contact, diffusion rates, and at the end of the process, expansion rates to be able to start thinking about the bonding between the glass surfaces.