Can anyone tell me the software name where I can measure the magnetic behavior of my input structure?

More Mohammad Zahidul Hossain Khan's questions See All

Please explain how the plastic input value should be considered from the true stress-strain curve for the bilinear elastoplastic material model ?

I am working on Abaqus/Explicit(Quasistatic ) for the deformation of the auxetic structure model. Please explain how the plastic input value should be considered from the true stress-strain curve...

05 August 2024 454 3 View

Binder for ZnO nanoparticles in graphite paste electrode?

I have been using paraffin, but the deposited ZnO still detach from electrode. What is the best binder to modify graphite paste electrode with ZnO nanoparticles?

03 August 2024 4,624 3 View

What is fitofthora instance of potatoes?

Now research fellow used it to prevent fungus in potato,may be potatoes gene effect.

02 August 2024 180 3 View

What is gangrine? Is there gangrine happened indie potato?

Please discuss someone told about fungus and allied others.

31 July 2024 3,372 3 View

If the emission of all greenhouse gases is stopped now, will the temperature of the earth continue to rise?

Here's a serious question: If we were to stop emitting all greenhouse gases right now, would the Earth's temperature start to cool down, or would the existing greenhouse gases continue to warm the...

30 July 2024 5,123 4 View

How gold procurement?

Please note it

29 July 2024 4,920 3 View

How gold procurement?

https://www.cleanteqwater.com/resources/case-studies/gold-mine-australia/

29 July 2024 5,161 1 View

Wrong out put for gmx x2top?

Dear users, I would like to simulate a zeolite structure in gromacs. I got the .cif file from IZA expanded in one direction in Materials Studio and exported a .pdb file. However, when I want to...

24 July 2024 367 4 View

Is there a good macro photography kit for on-site metallurgical investigation?

I am looking to purchase a photography kit for onsite metallurgical investigations, such as capturing photos of worn areas, hot tears, cold tears etc. Could anyone suggest me a good...

22 July 2024 3,490 2 View

Why not cow dung manure used in lie for artificial ?

Cow dung manure is more powerful than artificial fertilizer.

19 July 2024 7,392 7 View

Which type of compound does lamda max of 218 indicate in a uv-vis spectrum of a partially purified compound through column and TLC?

A crude extract of fungal culture using EtOH was subjected to column and TLC and partially purified compound was obtained. UV vis spectrum of the compound/s has max absorbance at 218nm. The...

11 August 2024 9,801 2 View

U you think We need a website software of Blackbody radiation law expert software?

A website software of Blackbody radiation law expert software can used through the following web site. http://39.105.188.151:3000/index

07 August 2024 1,706 0 View

How does grain and grain boundary affect the ceramic when studying its dielectric properties?

I am not able to get good literature and the physics behind how first these grains and grain boundaries arises out of no where when we make a pellet to study its dielectric properties and then how...

07 August 2024 5,177 3 View

How to understand this crystallographic phenomenon of low temperature crystals in zeolite?

During low-temperature testing, new diffraction peaks that appear could be indicative of several phenomena. In one of our tests, we observed notable new peaks around 40° and 45° in a specific...

06 August 2024 726 3 View

Can anyone explain why there is not any color bands in the middle portion of the tensile coupon?

Details of the Analysis. Static Analysis Composite Layup Continuum Shell Elements FRP Material (Elastic and Hashin Damage)

03 August 2024 8,538 4 View

Why do paired electrons atoms produce no magnetic field lines?

If you think of electrons with spin as bar magnets, you know bar magnets of opposite polarity as long as they're not occupying the same spatial location don't cancel out each other's magnetic...

03 August 2024 3,927 2 View

Can't spin-orbit coupling(SOC) be included in optical properties calculation in CASTEP?

I am currently using CASTEP version 2020. When I want to run optical properties calculations with spin-orbit coupling(SOC), I encounter the following error in a pop-up window before the job gets...

02 August 2024 2,890 0 View

How to correctly use the UTE and ZTE pulse sequences in Bruker's ParaVision software?

I am using a Bruker 600M solid-state NMR spectrometer with a Micro 2.5 microimaging system. The test sample is a tube of 1M LiCl aqueous solution, and the nucleus detected is 1H. I am trying to...

01 August 2024 9,227 1 View

Can a Conventional 50W visible LED Lamp Emit UV Light?

I'm researching light sources and their UV emissions. I'm curious if a 50W, 7500K conventional LED lamp emits any UV light. I found that a 200W tungsten lamp can emit up to 1.5 mW/cm² at 350 nm....

31 July 2024 3,843 7 View

How to select target material for X-Ray generation?

Generally, the target material is Mo, Co, Cu, Fe, Cr, etc, so on what basis should we choose this material?

31 July 2024 5,824 0 View

Muhammad Shahbaz Anwar

You can try OOMMF

Venkata Ramana Mudinepalli

You can go for OOMMF as suggested by Anwar or KERR microscopy.

They might be useful for your work.

Wish you good luck.

Mohammad Zahidul Hossain Khan

Dear Anwar and Venkata

Thank you very much for your response. Can you tell more. I have installed oommf but I have seen there input structure is mif format. I have no idea how can I convert my crystal structure to mif format.