I am working out soft magnetic properties of Fe-Si- B amophous ribbon. So, I'd like measure the specific heat of Fe-Si- B amophous ribbons. There are some references describing about this process. But, I'm not sure how can I take the reference curve. Can anyone help me?
Dr. Orozco's suggestion is good. however if you think of heating to get the temperature depependence, you have got to be careful. As you know crystallisation is a kinetic process so as one approches the crystallisation temperature you might get into the formation of metastable phase which would lead to error.
Of course, Dr. Krishnan rightly points that you should be careful not to go above the glass transition temperature or onset of crystallization as then you'll have crystallization processes. Besides the metastable effects pointed by Dr. Krishnan you would also be measuring a different phase, not the amorphous ribbon properties.