I am working on in-situ TEM fracture mechanics. My question is when the crack is propagating,how do the shear modulus of precipitates play a role?

Since the shear modulus of the matrix is different even if by few GPa , the precipitates has to play a role. Are they easily shearable or not?

12 June 2018 986 3 View