I’ve got Waspaloy went through cold forging and solution treatment under controlled atmosphere. Intergranular attack was pre-existing but the depth doubles after heat treatment at 1050 C. Any...
last month 9,957 3 View
Hi All, I would like to observe the 3D morphology of Fe-rich intermetallics in Al wrought alloy, e.g. AlFeMnSi, using SEM. Does anyone have experience or idea about what the best procedure would...
12 April 2022 7,326 4 View
Hi All, I am interested in fatigue testing of Al alloys in the gyga-cycle regime. If I use high frequency (up to 300 Hz), will I have faster localization of damage and lower fatigue strength...
03 July 2021 6,260 31 View
Dear friends, We approached toward SLM of a new Al-Zn-Mg alloy using single track experiment. The initial feedstock powder was ball-milled (not atomized). More than 10 tracks fabricated at...