The least thickness, of the polymer composite, that can be made by hand lay-up method to evaluate tensile and flexural properties ?

error in running a model in Abaqus

Excessive rotation of nodes in node set ErrNodeExcessRotation-Step1

17 August 2021 0 0 View

error in modelling model in Abaqus

Excessive rotation of nodes in node set ErrNodeExcessRotation-Step1

17 August 2021 0 0 View

MGL tools

20 June 2021 0 0 View

what is the simplest definition of ion exchange capacity

What this unit identifies for the ion exchange capacity ca. 0.92 meq. g-1. I am a newcomer in the membrane area. I just started. I highly appreciate your help

08 May 2021 0 0 View

what is the simplest definition of ion exchange capacity

What this unit identifies for the ion exchange capacity ca. 0.92 meq. g-1. I am a newcomer in the membrane area. I just started. I highly appreciate your help

08 May 2021 0 0 View

flexibility of polymers chain

effect of double bond on the flexibility of polymers

07 April 2021 0 0 View

i have some problem with chtMultiRegionSimpleFoam

--> FOAM FATAL ERROR: Maximum number of iterations exceeded From function Foam::scalar Foam::species::thermo::T(Foam::scalar, Foam::scalar, Foam::scalar, Foam::scalar (Foam::species::thermo::*)(Foam::scalar, Foam::scalar) const, Foam::scalar (Foam::species::thermo::*)(Foam::scalar, Foam::scalar) const, Foam::scalar (Foam::species::thermo::*)(Foam::scalar) const) const [with Thermo = Foam::hConstThermo >; Type = Foam::sensibleEnthalpy; Foam::scalar = double; Foam::species::thermo = Foam::species::thermo >, Foam::sensibleEnthalpy>] in file /home/ubuntu/OpenFOAM/OpenFOAM-4.1/src/thermophysicalModels/specie/lnInclude/thermoI.H at line 66. FOAM aborting #0 Foam::error::printStack(Foam::Ostream&) at ??:? #1 Foam::error::abort() at ??:? #2 Foam::heRhoThermo >, Foam::sensibleEnthalpy> > > >::calculate() at ??:? #3 Foam::heRhoThermo >, Foam::sensibleEnthalpy> > > >::correct() at ??:? #4 ? at ??:? #5 __libc_start_main in "/lib/x86_64-linux-gnu/libc.so.6" #6 ? at ??:?

24 March 2021 0 0 View

Formulation of polymer color flakes

I am writing to request some information for making polymer color flakes. I would appreciate the help.

17 March 2021 0 0 View

Can we classify HV and LV lines based on line length?

I have dataset which shows the length of power lines. I need to classify the lines based on the line length. Is there a rule to classify the High voltage (HV) and low voltage (LV) lines based on...

03 March 2021 4,116 4 View

Polymer composites suddenly solidifies?

I am making polymer composite by solvent mixing method. When I am trying to add filler solution in polymer solution it quickly get solidified. How to make them then uinform? It doesn't give time...

03 March 2021 7,540 4 View

Gurusideswar Sivanarutchelvan

You can refer ASTM standards D638 & D3039 (Tensile) and D790 (Flexural)

Muhammad Arslan Mehmood Hunjra

Thickness or number of layers in fiber reinforced composites have no effect on tensile properties. With increasing thickness load sustained by sample will increase but strength will remain the same. If you are using hand layup then you should be concerned about surface finish and uneven thickness which will lead to doubtful results. Same is the case with flexural testing but inter-laminar interactions should be considered while concluding results.